T 1677/13 13-02-2015

1. The appeal is admissible.

2. As indicated in section VIII above, the appellant, although duly summoned, was absent from the oral proceedings. In accordance with Article 15(3) RPBA, the appellant was treated as relying only on their written case.

Article 100 (c) EPC

3. The deletion of the term "about" before numerical values does not infringe Article 123(2) EPC according to normal practice under the Case Law of the Board of Appeals, unless the skilled person would understand, from the whole content of the application as filed, that an exact value as such could not have been meant, as was the case in T 934/96. That decision concerns a situation in which a value defined to be "about 15%" ("ca. 15%") in an explanation concerning a figure could not be taken as an upper limit of exactly 15% in a claim since it would define subject-matter that was in contradiction with the information provided by said figure. In other words, the whole context of the disclosure concerning the value of about 15% did not provide a direct and unambiguous basis for defining an upper value of 15% in the claim.

3.1 In the present case, the range "between 30 g/10 minutes and 45 g/10 minutes" is clearly and unambiguously disclosed in the expression "from about 30 g/10 minutes to about 45 g/10 minutes" defined on page 9, third paragraph of the application as filed, representing the more preferred range for component 2 of the blend. Its introduction in claim 1 as originally filed does not lead to any contradiction between the subject-matter of claim 1 as granted and the passage specifying the range "from about 30 g/10 minutes to about 45 g/10 minutes" because that range is not defined in a specific context, but is clearly meant to be generally applicable, i.e. to the general context of claim 1 as filed. Thus, decision T 934/96 is not applicable to the present case.

3.2 In view of the above, the claimed subject-matter complies with Art 123(2) EPC.

Article 100 (b) EPC

4. For sufficiency of disclosure the question needs to be answered whether the patent in suit provides sufficient information to enable the skilled person to perform the invention as defined in the claims, taking into account common general knowledge; in the present case, to obtain the claimed blends and fibres or objects made therewith.

4.1 Regarding the definition of the polyethylene components (a) and (b) as defined in claim 1, those components are either known or their manufacture, conventional in the art, does not necessitate any inventive skill. Also measurement of the density and melt flow rate of the obtained polymers is conventional, as shown for example by D7 and D9. As to the claimed compositions, they can be obtained by blending the two components as shown in paragraph [0031] and Example 1 of the patent in suit, so that the skilled person is in a position to obtain the composition. Furthermore, the density and melt flow rate of the mixture can be either approximated using the conventional relationships, as in document D1 (page 4, lines 10-17), or measured using the methods described in D7 and D9. The methods to be employed in order to prepare articles or polymeric mixtures from those polymeric blends as defined in claims 7 to 11, are also known to the skilled person, which has not been denied by the appellant, so that the subject-matter defined in any of claims 1 to 11 is sufficiently disclosed.

4.2 The appellant's objection regarding lack of sufficiency refers to an ambiguity and/or difficulty in determining the melt flow rate or density of the polymeric components of the claimed composition/articles, because components thereof were held to be difficult to separate and the values of the melt flow rate might depend on the type of procedure used within the method ASTM D 1238. The appellant's objection therefore concerns the determination of the exact limits of the claimed subject-matter, in particular in view of the question how it can be determined whether a mixture or article falls within the ambit of the present claims. That question has nothing to do with the question whether the skilled person can obtain the claimed blends and fibres or objects made therewith and is a matter of clarity (Article 84 EPC), not of sufficiency of disclosure(Article 83 EPC). Since the appellant's objection does not arise out of any amendment made in opposition or appeal proceedings, any lack of compliance with the requirements of Article 84 EPC cannot be objected to. The appellant has not shown that a certain ambiguity in determining the exact limits of the claim would prevent the skilled person from obtaining the claimed subject-matter.

4.3 In view of the above considerations, the requirements of Art. 83 EPC are complied with.

Article 100 (a) EPC - Novelty

5. The question to be answered for novelty is whether any of D1 or D3, cited by the appellant as anticipatory prior art, provides a clear and unambiguous disclosure of the claimed subject-matter.

5.1 D1 describes a blend of linear polyethylenes suitable for spunbonding at throughput rates of 1,0 to 1,2 grams/minute/hole, at linear spinning velocities of at least 3500 meters per minute, to produce fiber sizes of less than 3.0 denier/filament, comprising

high molecular weight linear polyethylenes having a MFR value within the range between 0,5 to 25 g/10 min. and a density above 0,91 g/cm**(3), and

low molecular weight linear polyethylene having a MFR value within the range between 25 to 300 g/10 min. and a density above 0,91 g/cm**(3)(claim 1).

D1 page 2, line 56 to page 3, line 3, describes a density of the first component in the range of 0,91 to 0,96 g/cm**(3)and a melt index of less than 25g/10 min., preferably less than 20 g/10 min. **()The density of the second component is disclosed to be in the range of 0,91 to 0,96 g/cm**(3)and its melt index as greater than 25 g/10 min., preferable greater than 40 g/10 min (page 3, lines 7 to 10). The density and melt index of the blend of D1 are from 0,91 to 0,96 g/cm**(3)and from 25 to 300 g/10 min., respectively (claim 2).

Those passages do not disclose that the low molecular weight component of the blend has a density which is equal to or higher than that of the high molecular weight component of the blend, let alone that those have to be comprised in the ranges of 0.900 g/cm**(3) to 0.935 g/cm**(3) and 0.935 g/cm**(3) to 0.965 g/cm**(3), respectively. Those passages of D1, cited by the appellant, merely indicate that both components should have a density in the range of 0.91 g/cm**(3) to 0.96 g/cm**(3). Hence, the objection for lack of novelty over the disclosure of D1 fails to convince.

5.2 D3 describes a fiber having a diameter in a range of from 0,1 to 50 deniers which is prepared from a polymer blend, wherein the polymer blend comprises:

A. from 0,5 percent to 25 weight percent (by weight of the polymer blend) of a first polymer which is a homogeneous ethylene/alpha-olefin interpolymer having:

i. a melt index of from 0,5 to 100 gram/10 minutes,

ii. a density of from 0,850 to 0,920 gram/centimeters**(3), and

B. a second polymer which is an ethylene homopolymer or an ethylene/alpha-olefin interpolymer having:

i. a melt index of from 0,5 to 500 gram/10 minutes, and

ii. a density which is at least 0,01 gram/centimeters**(3) greater than the density of the first polymer, wherein the fiber is bondable at a temperature of less than 165°C (claim 1).

The first component of D3, which is a homogeneous linear or substantially linear ethylene polymer, has a density of at least 0.850 grams/centimeters**(3), preferably at least 0.855 grams/centimeters**(3), and more preferably at least 0.860 grams/centimeters**(3); and typically no more than 0.920 grams/centimeters**(3), preferably no more than 0.900 grams/centimeters**(3), more preferably no more that 0.890 grams/centimeters**(3), and most preferably no more than 0.880 grams/centimeters**(3) (column 6, lines 47 to 56). The melt index of the first component is generally at least 0.1 grams/10 minutes, preferably at least 0.5 grams/10 minutes, more preferably at least 1 grams/10 minutes; generally no more than 100 grams/10 minutes, preferably no more than 30 grams/10 minutes, more preferably no more than 10 grams/10 minutes, even more preferably no more than 5 grams/10 minutes, and most preferably no more than 1,5 grams/10 minutes (D3, column 7, lines 9 to 19).

Regarding the second component, when it is an ethylene polymer, it will have a density which is at least 0.01 grams/centimeters**(3), preferably at least 0.03 grams/centimeters**(3), more preferably at least 0.05 grams/centimeters**(3), and most preferably at least 0.07 grams/centimeters**(3) greater than that of the first polymer. The second polymer will typically have a density of at least 0.880 grams/centimeters**(3), preferably at least 0.900 grams/centimeters**(3), more preferably at least 0.935 grams/centimeters**(3), even more preferably at least 0.940 grams/centimeters**(3) and most preferably at least 0.950 grams/centimeters**(3)(column 6, lines 56 to 67). Its melt index is generally at least 0.5 grams/10 minutes preferably at 3 grams/10 minutes, and more preferably at least 5 grams/10 minutes. In the case of melt blown fibers, the melt index for the second polymer is preferably at least 50 grams/10 minutes, more preferably at least 100 grams/10 minutes; preferably no more than 1000 grams/10 minutes, more preferably no more than 500 grams/10 minutes. For spunbond fibers, the melt index of the second polymer is preferably at least 15 grams/10 minutes, more preferably at least 25 grams/10 minutes; preferably no more than 100 grams/10 minutes, more preferably no more than 35 grams/10 minutes For staple fibers, the melt index of the second polymer is preferably at least 8 grams/10 minutes, more preferably at least 10 grams/10 minutes; preferably no more than 35 grams/10 minutes, more preferably no more than 25 grams/10 minutes. For flash spun fibers, the melt index of the second polymer is preferably at least 0.1 grams/10 minutes, more preferably at least 0,5 grams/10 minutes; preferably no more than 3 grams/10 minutes, more preferably no more than 2 grams/10 minutes (D3, column 7, lines 20 to 37).

There is no indication that those passages, cited by the appellant, should be read in combination, in particular in the combination now being claimed. In fact, in view of the broad disclosure of D3, such a combination of the various possibilities disclosed in D3, providing various preferred lower and upper limits for the density and melt indices of the two components, can only be arrived at with knowledge of the subject-matter now being claimed. Moreover, the argument that the density and melt index of the blend as defined in the patent in suit could be calculated from the values of the first and second components disclosed in said passages of D3 is not supported by any evidence. Not only did the appellant not provide such calculation, but also do the cited passages of D3 not disclose any proportion for the first and second resin components, which is necessary in order to carry out such calculation. Hence, no case has been made for lack of novelty over D3 either.

5.3 For the above reasons, the claimed subject-matter complies with Art. 54 EPC.

Article 100 (a) EPC - Inventive step

6. The patent in suit concerns polymeric blends comprising a mixture of two different polyethylene resins, which blends are used to produce fibres and nonwoven materials comprising said fibres (paragraph [0001]). D1 which concerns spunbonded webs or fabrics prepared using similar blends (see claims 1 and 9, page 4, lines 18-32), was considered by both parties to represent the closest prior art, in particular in view of the blend components disclosed on page 2, line 55 to page 3, line 13 of D1. The Board sees no reason to take a different view and sees D1 as an appropriate starting point for assessing inventive step.

6.1 The respondent submitted that the problem solved by the claimed subject-matter over the blends of D1 was to provide polyethylene material suitable for use in a fibrous nonwoven that was readily extensible and had an improved abrasion resistance (low fuzz).

That line of argument for inventive step was brought forward for the first time at the oral proceedings before the Board, i.e. at a very late state of the appeal proceedings. Concerning inventive step the respondent had not submitted any arguments in writing, but had merely indicated to agree with the conclusion reached by the Opposition Division, starting from D1 as the closest prior art. In view of the new argument, the conclusion has to be drawn that the respondents' written submissions were not complete and did not contain all the facts, arguments and evidence upon which it relied in support of its case, contrary to Article 12(2) RPBA. Admitting the respondent's new line of argument would have the effect of introducing a crucial point in the assessment of inventive step, namely an advantage over D1 allegedly brought about by the claimed subject-matter, that had not been considered in the contested decision and in appeal until the oral proceedings.

6.2 The Respondent's failure to submit this crucial point in the assessment of inventive step at an earlier stage deprived the appellant of the opportunity to present their comments thereon and/or to reconsider their intention not to attend the oral proceedings. The introduction of this new line of argument at the oral proceedings - in the absence of the appellant - raised the question whether the board could arrive at a decision on the basis of this belated submission without contravening the respondents' right to be heard, or whether the proceedings should be adjourned. Therefore, the Board does not admit the respondent's new line of argument to the proceedings and decides to assess inventive step merely on the basis of the argumentation submitted by the parties in writing (Article 13(3) RPBA).

7. The statement of grounds of the appeal does not provide any indication that the appellant contests that the claimed blends provide a successful solution to the problem of providing polymeric blends that, compared to those of D1, result in fibres exhibiting increased extensibility. Concerning the issue of inventive step, the letter of 5 June 2014 in reply to the respondent's rejoinder only contains a general reference to earlier submissions made before the first instance. Such a general reference cannot replace an explicit indication that the problem as formulated in the contested decision is not considered to be successfully solved, let alone arguments to support that view. It cannot be expected that the Board substitutes itself for the appellant and, in breach of the principle of equal treatment of the parties, investigates, in lieu of that party, whether the experimental data provided in the patent in suit constitute sufficient evidence that the problem indicated in the contested decision is successfully solved.

Under those circumstances and in the absence of any apparent reason for a contrary finding, the claimed subject-matter is considered to constitute a successful solution to the problem of providing polymeric blends that result in fibres exhibiting increased extensibility.

8. It remains to be decided whether or not the skilled person, starting from D1 and wishing to solve the above defined problem, would have been guided by the available prior art to use a blend as defined in claim 1 of the patent in suit, characterized by, among other things, a first component having a density between 0.900 g/cm**(3) and 0.935 g/cm**(3) and a melt flow index between 5 g/10 minutes and 25 g/10 minutes and a second component having a density between 0.935 g/cm**(3) and 0.965 g/cm**(3), its melt flow index being between 30 g/10 minutes and 45 g/10 minutes.

8.1 In this respect, the appellant referred to the blends described in D3, from column 6, line 47 to column 7, line 37. That passage, however, merely describes preferred upper and lower limits for the density and melt flow index of each of the first and second component of the blend. Those preferences provide a pointer towards the component with the lower density, preferably 0,860 to 0,880 g/cm**(3,) to have a melt index preferably of 1 to 1,5 g/10 minutes, i.e. both ranges are below those defined in claim 1 of the patent in suit. Moreover, the appellant did not provide any explanation, for example on the basis of calculations, that showed that the modification of one of the components of the blend disclosed in D1 using a component of D3, would result in a blend necessarily having the density and melt index required by present claim 1. In the absence of any indication to this effect, let alone any indication in that passage that such a modification would result in an improvement of the extensibility of the fibres made with the blend, it cannot be concluded that, starting from D1, D3 renders the claimed subject-matter obvious.

8.2 Therefore, no case has been made by the appellant that, having regard to the state of the art, the subject-matter of claim 1 was obvious to the skilled person. Consequently, the subject-matter of present claim 1 and by the same token that of dependent claims 2 to 5 meets the requirements of Article 56 EPC.

9. As the appellant did not make any submissions in relation to claims 6 to 11 which define products comprising a polymeric blend according to claim 1, the Board also concludes that the subject-matter of claims 6 to 11 was not obvious to the skilled person (Article 56 EPC).