T 0641/23 18-10-2024

Main request

1. Article 123(2) EPC

1.1 The opposition division concluded in their decision that there was no basis in the application as originally filed for the definition of the semiconductive composition used in the measurement of the electrical DC-conductivity of the crosslinked composition as comprising "a polymer and carbon black" (decision under appeal, page 5). The appellant contended in appeal that the amendment in claim 1 of the main request did not infringe the requirements of Article 123(2) EPC.

1.2 According to Article 123(2) EPC the European patent application or the European patent may not be amended in such a way that it contains subject-matter which extends beyond the content of the application as filed. According to the "gold standard" (G 2/10, OJ 2012, 376) for assessing compliance with Article 123(2) EPC any amendment to the parts of a European patent application or of a European patent relating to the disclosure (the description, claims and drawings) is subject to the mandatory prohibition on extension laid down in Article 123(2) EPC and can therefore, irrespective of the context of the amendment made, only be made within the limits of what a skilled person would derive directly and unambiguously, using common general knowledge, and seen objectively and relative to the date of filing, from the whole of these documents as filed (G 3/89, OJ 1993, 117; G 11/91, OJ 1993, 125). After the amendment the skilled person may not be presented with new technical information (G 2/10).

1.3 The amendment in dispute concerns the presence of a combination of a polymer and carbon black in a semiconductive composition that is brought into contact with a plaque sample of the crosslinked polymer composition prior to the measurement of its electrical DC-conductivity. While the semiconductive composition disclosed in operative claim 1 is not as such a component of the crosslinked polymer composition, it is nevertheless an essential part of its characterization since it is a component used in the preparation step of a sample on which the electrical DC-conductivity is measured. It is also apparent from the passage on page 5, lines 8-23, that the electrical DC-conductivity of the crosslinked polymer composition has in fact changed after having been contacted with a semiconductive composition. That is confirmed by the examples of the patent in suit which show that the electric conductivity of a plaque of a crosslinked polymer compositions has changed significantly after contact with a semiconductive layer at 70 C for 24 hours (see in particular the data at the bottom of Table 1). The semiconductive composition used during the determination of the electrical DC-conductivity according to operative claim 1 therefore has an impact on the measured property which defines the crosslinked polymer composition. In view of this, the components of the semiconductive composition, including the polymer and carbon black, brought into contact with the crosslinked polymer composition are also part of the definition of crosslinked polymer composition of operative claim 1 even if they are not constitutive components of that composition.

1.4 Claim 1 as originally filed defines the same steps leading to the measurement of the electrical DC-conductivity as claim 1 of the main request, but the semiconductive composition used in the measurements is not further defined. The critical question is therefore whether the application as originally filed contains a basis for the definition of the semiconductive composition as one comprising a polymer and carbon black.

1.5 The semiconductive composition used in the determination of the electrical DC-conductivity of the crosslinked polymer composition is mentioned in the passage relating to the DC conductivity method on pages 28-29 of the application as originally filed. The paragraph on page 28, lines 16-21 describes that the DC conductivity method involves the preparation of plaques by compression moulding pellets of a semiconductive polymer composition.

1.6 The passage bridging pages 28 and 29 further mentions the role of the semiconductive polymer compositions in the determination of the electrical DC-conductivity of the polymer compositions to be tested. In a step referred to as the conditioning step, one plaque, consisting of the crosslinked polymer composition to be tested, and one plaque, consisting of the semiconductive polymer composition, were stored together in direct contact with each other in a closed aluminium bag at 70 C for 24 hours. After the conditioning step the plaques were separated and DC conductivity measurement was performed on the plaque, consisting of the crosslinked polymer composition to be tested. The method for the measurement of the DC-conductivity disclosed in the description of the application as originally filed corresponds to that defined in claim 1 of the main request but apart from lines 16-17, 24 and 33 on page 28 mentioning the use of a semiconductive polymer composition (emphasis added), there is no further disclosure of the material of the composition and in particular no mention of carbon black being present in the semiconductive composition.

1.7 Carbon black in combination with a polymer as part of a semiconductive composition is disclosed solely on page 21, lines 15-21 of the application as originally filed. That passage, however, belongs to the chapter "End uses and end applications of the invention" starting on page 19, line 8 which concerns the use of crosslinked polymer compositions and semiconductive compositions for the production of power cables. It is therefore apparent that the references to semiconductive compositions in that passage only pertain to outer and inner layers of the power cables and not to the semiconductive compositions used in the DC-conductivity method described on page 28 of the application as originally filed.

1.8 In that respect the appellant argued that the skilled reader of the application as originally filed would have understood that the passage disclosing semiconductive compositions comprising carbon black for power cables on pages 20-22 and the passage on the DC-conductivity method on pages 28-29 referred to the same semiconductive composition (statement of grounds of appeal, section 18). This would be due to the fact that the test conditions are meant to mimic the semiconductive layers of a cable in use. The Board, however, does not find support for that relationship in the application as originally filed. In this respect, the passage on page 8, lines 21-30 of the application as originally filed which mentions layered structures comprising a polymer layer and at least one semiconductive layer adjacent to the polymer layer uses the indefinite article "a" when it discloses the semiconductive composition contacted with the polymer composition for 24h at 70 C, indicating that that semiconductive composition is not necessarily defined by the semiconductive composition of the layer. In addition the semiconductive composition comprising carbon black is mentioned on pages 20-22 as just one example of a possible composition for the layers and not as the one which is necessarily selected for use. Therefore, even if the skilled person considered the measurement as meant to mimic the situation in use, no link to the necessary use of carbon black in the measurement would be present.

1.9 The appellant additionally considered that the examples of the application as originally filed supported the presence of carbon black in the semiconductive composition used in the DC-conductivity method (statement of grounds of appeal, section 20). It was in particular argued that the examples of the application as originally filed disclosed the use of a commercially available semiconductive polymer composition based on a commercially available product (LE0550) (page 32, line 6 of the application as originally filed). That commercially available product LE0550 would comprise, alongside a polymer, carbon black, as shown in D8 (page 56, line 24), D13 (page 49, line 2) and D18 (paragraph "special features"). The disclosure of the examples, however, is specific to the compositions disclosed therein. There is, beyond that example, no generalizable teaching in the application as originally filed from which it could be concluded that the semiconductive compositions used in the characterization of the crosslinked polymer compositions according to operative claim 1 contained a polymer and carbon black in general.

1.10 The appellant further argued that the presence of a polymer and carbon black in semiconductive compositions was part of the common general knowledge of the skilled person. The Board, however, does not find support for that argument in the evidence discussed in appeal.

1.11 The Board therefore comes to the conclusion that claim 1 of the main request does not meet the requirements of Article 123(2) EPC.

Auxiliary request 1

2. Article 123(3) EPC

2.1 Claim 1 of auxiliary request 1 concerns a crosslinked polymer composition as disclosed in claim 1 of the main request but does not define the semiconductive composition used in the measurement method as comprising a polymer and carbon black.

2.2 Granted claim 1 defines a crosslinked polymer composition in which the semiconductive composition used in the measurement method contains a polymer and carbon black. The opposition division concluded that claim 1 of auxiliary request 1 did not meet the requirements of Article 123(3) EPC in view of that deletion (section 6 of the decision under appeal).

2.3 The appellant argued in appeal that the amendment made in claim 1 of auxiliary request 1 does not extend the protection conferred by the patent in suit (section 40 of the statement of grounds of appeal). It is apparent from section 41 of the statement of grounds of appeal that the argument of the appellant relied on the premise that the semiconductive composition was not part of the crosslinked polymer composition defined in claim 1 but instead was part of the definition of the measurement of a parameter of that composition. As set out above under point 1.3, the semiconductive composition is disclosed as having an effect, by contact for 24h at 70°C prior to measurement, on the electrical DC-conductivity of the crosslinked polymer composition. In view of this, the components of the semiconductive composition also have an impact on the measurement made, especially if these components are expected to participate in the properties of the semiconductive composition itself. Deleting the compulsory presence of a polymer and carbon black in claim 1 of auxiliary request 1 therefore extends the scope of the claim beyond the extent of protection of granted claim 1. In this respect, the Board finds that a reading of claim 1 of auxiliary request 1 as implying that the condition on the electrical DC-conductivity should be met for any semiconductive composition (including one comprising a polymer and carbon black) is not in agreement with the wording of claim 1, nor appears to be technically and practically reasonable. For these reasons, the Board comes to the conclusion that claim 1 of auxiliary request 1 does not meet the requirements of Article 123(3) EPC.

Auxiliary requests 2-9

3. Article 123(2) EPC

3.1 It is apparent that claim 1 according to auxiliary requests 2-9 contains the same amendment as claim 1 of the main request that was found by the Board to infringe on Article 123(2) EPC. In this respect, it was acknowledged by the appellant that, if the Board came to the conclusion that that amendment was not allowable under Article 123(2) EPC for the main request, then the same conclusion would also apply to claim 1 of auxiliary requests 2-9. For this reasons the Board comes to the conclusion that claim 1 of auxiliary requests 2-9 does not meet the requirements of Article 123(2) EPC.