T 0740/91 15-12-1993

1. The appeal is admissible.

2. Admissibility of Amendments

2.1. The only amendments introduced by the Respondent are the two further limitations in Claim 1, that the epoxy compound is applied to the yarn and cured while the yarn has a twist of fewer than 10 turns per meter, and the replacement of the upper limit of 5% of cured epoxy compound by the much lower limit of 0.6%. The first of these two limitations was not subject to any dispute, having been clearly disclosed in the application as filed at page 5, lines 18 to 21, corresponding to page 3, lines 47 to 49 of the granted patent. Although it was argued by the Appellant that the 0.6% limit is not disclosed in Example III, which refers to the yarn prior to heating having picked 0.6% by weight of uncured epoxy compound, suggesting that the amount of the cured compound must have been significantly less due to loss by volatilisation, the Respondent, while accepting that some small loss could occur, maintained that the true level of 0.57% had legitimately been rounded up to the single figure of 0.6%, which corresponded with the single figure given at page 3, line 45 for the amount of uncured epoxy compound applied.

2.2. In the absence of any firmer justification for the 0.6% upper limit, the Board would have been prepared to accept that argument. As is clear from the Table at page 6 of the Respondent's letter of 28 November 1989, the patent in suit includes a total of 14 Examples of applying an epoxy compound in accordance with the alleged invention, and in all of them the amounts fall within the range of 0.32% to 0.60%, albeit that the actual value of 0.6% given in Example III was accepted by the Respondent at the oral proceedings as having been rounded up to that figure.

2.3. The Respondent did not seek to rely on the disclosure of Example IV, explaining that although there was an explicit disclosure at page 9, line 63 that:

"The yarn thus treated [i.e. in the cured condition] contained 0.6% by weight of resin."

their laboratory records, details of which were contained in the above-mentioned Table, showed that that figure was not correct, and that the true figure was 0.49%. The figure of 0.6% given in the patent in suit was admitted by the Respondent to have been inserted in error in place of the true figure of 0.49%.

2.4. That gives rise to the issue of law, of whether an actual disclosure in an application as filed, if later accepted by the patentee as having been included in error, can nonetheless legitimately be used as the basis for making an amendment. Looking at the wording of Article 123(2) EPC, it is observed that the test which has to be applied is to ask whether the amendment has the effect that the patent when amended contains subject-matter which extends beyond the "content of the application as filed". In relation to the present Example IV, what was in the application as filed was an explicit disclosure of an amount of epoxy compound on the fibre after curing at a level of 0.6%. The fact that the figure given in that Example was wrong does not alter the situation that it was actually disclosed, and credibly disclosed, in the application as filed. In these circumstances the Board holds that it may be relied on as the basis for the new upper limit in Claim 1.

2.5. This interpretation of Article 123(2) EPC is consistent with the underlying intention of that Article, which is to protect the public from being faced at a later stage with claims which are wider in their scope than what was disclosed in the application as filed, and published for the information of the public, including the applicant's competitors.

2.6. Any such competitor of the present Respondent, who had read the application as first published, and who formed the view that the originally claimed range of 0.1 to 5% was too wide in the light of the prior art, such as document (1a), and who thought that the broad claim could not validly be sustained, would then have needed to consider what figure might reasonably be introduced as an upper limit. He would have seen at once that the highest figure for the cured epoxy resin given in any Example was the 0.6%, clearly disclosed in Example IV, and therefore could not have been taken by surprise if the upper limit of 5% were later to be reduced to 0.6% as a result of a limiting amendment, whether made during examination or in the course of any later opposition. The fact that the figure was wrong would be unknown to competitors, and therefore could not influence their judgment.

2.7. It follows that the Board accepts the 0.6% upper limit as being substantiated both by the rounding up of the true level in Example III, and more particularly by its specific disclosure in Example IV.

3. Novelty

3.1. Novelty is challenged in the light of the disclosure of document (1a). Example 2 of that citation describes the preparation of poly-p-phenyleneterephthalamide fibres from the polymer solution. These fibres are described as being provided with a surface coating of an epoxy resin, which is obtained from an aqueous solution containing 2.5% of triglycidylisocyanurate. After a squeezing step, the amount of epoxy compound is said to be about 1% based on the dry weight of the fibre.

3.2. According to the general description in document (1a) (page 15, paragraph 2), the solution or dispersion of the epoxy compound may have a concentration of 1 to 10%. As argued by the Appellant, by using a concentration of 1%, instead of the 2.5% disclosed in Example 2, one would expect to obtain a significantly smaller amount of epoxy compound on the fibre than the 1% there disclosed, and possibly as little as 0.6% or less. Thus novelty was lacking.

3.3. In answer, the Respondent contended that the concentration of the aqueous solution ought not to be considered in isolation. There was no basis for the assumption that, e.g., a 50% reduction in concentration of the epoxy compound in the coating solution would result in the amount of cured epoxy compound on the yarn being reduced by 50%. That such an assumption is invalid is demonstrated by comparing Example 2 with Example 1. In Example 1, an aqueous dispersion containing 15% of an epoxy compound (i.e. 6 times as much as in Example 2) was used, but the amount of cured epoxy compound on the fibre was only 1.5%, i.e. only 50% more. This shows that by carrying out Example 2 using a solution having a lower proportion of epoxy compound, the amount of epoxy resin deposited on the fibre may well be less than 1%, but there is no evidence that the amount could be as little as 0.6% or less. In the absence of any experimental evidence directed to this issue by the Appellant, the Board follows the decision T 219/83 "Zeolites/BASF" OJ EPO 1986, 211 (Reasons point 12, paragraphs 4 and 5), in holding that where a party fails to substantiate an allegation of fact, and the Board is unable to establish the facts of its own motion, it is that party who loses thereby. Accordingly, this issue has to be resolved against the Appellant, and the objection that there is a lack of novelty on the basis of an inevitable result when carrying out a modified variant of Example 2 must be rejected.

3.4. In fact it is very doubtful whether in the context of document (1a) it is legitimate at all to treat the general teaching at page 15 of using 1 to 10% concentration of the solution or dispersion of epoxy compound as being of general applicability to each and every one of the wide variety of fibres and epoxy compounds disclosed in that citation. As is evident from the wording of Claim 1 of document (1a) and the description (page 5, paragraph 3 to page 9, paragraph 1) the multifilament yarns can be obtained from an aromatic polyamide as well as from an aromatic polyhydrazide. Moreover, the list of epoxy compounds regarded as suitable (page 10, paragraph 4 to page 11, paragraph 1) includes several classes of polyepoxides, such as polyglycidyl ethers of aliphatic polyols, polyglycidyl ethers of polyphenols, epoxidised unsaturated cycloaliphatic compounds, and heterocyclic compounds containing epoxy groups. This broad definition contrasts with the specific type of compounds envisaged in the patent in suit (page 3 lines 17 to 21) and used in all its examples, viz., polyglycidyl ethers of aliphatic polyols.

3.5. It is therefore reasonable to assume that the wide range of concentration of 1 to 10% at page 15 takes into account the many embodiments encompassed by the disclosure of document (1a), and it is therefore not legitimate to interpret the specific figures given in Example 2 as being subject to modification in accordance with the full breadth of the general teaching at page 15.

3.6. For these reasons the Board concludes that the figure of 0.6. in Claim 1 in the patent in suit is a distinguishing feature over the disclosure of document (1a). There is therefore no overlap between the claimed subject-matter and the disclosure of document (1a), and consequently the present case is not comparable with the situation dealt with in the decision T 12/90 (23.8.1990) referred to by the Appellant's representative at the oral proceedings, where such overlap was found to exist (Reasons point 2.12).

4. The Closest Prior Art

Like the Opposition Division and the parties, the Board takes the view that document (1a) represents the closest state of the art. As mentioned above when dealing with the issue of novelty, the amount of cured epoxy compounds on the yarns described in Examples 1 and 2 of document (1a) is 1.5 and 1% by weight. Although these multi-filament yarns are said to have good bundling properties which make them suitable for reinforcing applications (page 4, paragraph 3 and page 20, paragraph 2), their mechanical properties are not optimal; in particular the tenacity, elongation at rupture, and initial modulus cannot be regarded as satisfactory.

5. The Problem

In view of this shortcoming, the technical problem underlying the patent in suit can be regarded as the provision of a multifilament yarn of aromatic polyamide showing an improvement of the above-identified mechanical properties.

6. Its Solution

6.1. According to the patent in suit, this is achieved by reducing the amount of cured epoxy compound on the yarn to a range between 0.1 and 0.6% by weight. Both in its written and oral arguments, the Appellant has contended that this problem cannot effectively be solved by the claimed subject-matter.

6.2. Together with the statement of grounds of appeal, the Appellant filed a separate experimental report in which yarns obtained from an aromatic copolyamide prepared from terephthalic acid, p-phenylenediamine, bis(aminophenoxy)benzene and dimethylbenzidine were treated respectively with epoxy compositions containing the following ingredients:

A: 50% by wt. of a mixture of di- and triglycidylether of glycerine,

44.4% by wt. Leomin OR (Trade mark),

5.6% by wt. piperazin as hardener.

B: 50% by wt. of tetraglycidyl ether of tetrapropylene glycol,

44.4% by wt. Leomin OR (Trade mark),

5.6% by wt. piperazin as hardener.

6.3. These two compositions were each applied to 6 test yarns at such rates that the amounts of cured resin on the test yarns were 0.85%, 0.70%, 0.55%, and 0.40%, there being comparative runs with uncoated yarns, one subject to, and the other not subject to, the same heat treatment as the coated yarns.

6.4. The results purport to show that the mechanical properties of the so-treated yarns in terms of breaking strength and elongation at rupture are not significantly affected, either by the presence or absence of the epoxide coating, or by the quantity of the coating applied.

6.5. In its counterstatement filed on 13 March 1992, the Respondent contested the validity of these experiments on the ground that the relative amounts of the three amines in the fibre composition were not identified, so that it was uncertain whether the experiments were conducted on a known fibre at all, and the results were incapable of being repeated by the Respondent. Furthermore, the Respondent drew attention at the oral proceedings to certain questionable figures in the numerical results shown in the Appellant's experimental report, which left the Board in some doubt as to the reliability of the results obtained. Although the Respondent objected that there was no indication of whether the epoxy compounds had been applied from an aqueous solution, the Appellant assured the Board that although not so stated in the experimental report, that was the case.

6.6. Under these circumstances, the Board can only rely on the data submitted by the Respondent at page 4 of its letter of 1 Augsut 1990. With a view to demonstrating that there is a significant improvement in working within, as contrasted with outside, the claimed upper limit of 0.6%, the experimental report on that page contrasted the mechanical properties of a yarn A with 0.49%, with yarn B having 0.98%, of deposited cured epoxy compound, and showed the following results:

Yarn Cured epoxy Tenacity Elongation at Initial

compound on (cN/dtex) rupture modulus

the yarn (%) (cN/dtex)

(wt.-%)

A 0.49 17.4 3.11 530

B 0.98 14.1 2.76 490

6.7. The Board has also taken into account the experimental data contained in the patent in suit at Table F on page 11, showing that the problem is solved, in the sense that better mechanical properties are attained by applying an epoxide coating, not at a rate such as 1% which is disclosed in document (1a), but instead in the significantly smaller proportions falling within the claimed limits.

6.8. On that basis the Board concludes that the combination of features according to Claim 1 provides an effective solution to the above-defined problem.

7. Inventive Step

7.1. It remains to be decided whether the claimed subject-matter involves an inventive step.

7.2. As indicated by the Board during the oral proceedings, none of the documents cited by the Appellant would suggest to the skilled worker that an improvement in the desired mechanical properties is attainable by the application onto the fibres here under consideration of a smaller proportion of epoxy compound than had previously been contemplated. While it may be true, as was argued by the Appellant, that the skilled worker would consider keeping the quantity of epoxy compounds as low as possible having regard to their toxicity, there is no suggestion in the prior art, and it was not to be expected, that a positive effect on the mechanical properties of the yarn could be obtained by using a smaller proportion of epoxy compound than had previously been suggested. The Board has not lost sight of the fact that document (1a) was published some six years before the priority date of the application in suit, and that throughout that period, the incentive to minimise the use of epoxy compound on the ground of their potential toxicity must have existed. If the step proposed in the patent in suit had been obvious, the Board would have expected the beneficial effect on the meachanical properties of the yarn to have come to light sooner.

7.3. By finding that reducing the amount of epoxy compound on the fibres is capable of producing an unexpected positive effect, and by finding a solution to the problem identified above, the Respondent made a worthwhile contribution to knowledge in this art, which merits recognition as an inventive step. The Board is therefore satisfied that Claim 1 of the patent in suit involves an inventive step.

7.4. Claim 1 being inventive, the same applies to dependent Claims 2 to 12, which are directed to preferred multi- filament yarns according to Claim 1, further to Claims 13 to 22, which concern various objects obtained from the yarn as defined in Claim 1, as well as to Claims 23 to 32, which deal with a process for the manufacture of a multi-filament yarn according to Claims 1, and whose patentability is supported by that of the main claim.